Advanced Tools For Characterizing HMA Fatigue Resistance
MetadataShow full item record
Accurately and efficiently characterizing the material properties of hot mix asphalt (HMA) is critical to the design and development of pavements that can experience repeated loading for long periods of time and resist fatigue cracking. The Calibrated Mechanistic with Surface Energy (CMSE) method of design to preclude this primary type of distress requires that the HMA material be tested using the Relaxation Modulus (RM) and Repeated Direct Tension (RDT) tests to determine the material properties required for accurate calculations. The RM test requires considerable time to complete and provides results with relatively high variability. Further research has lead to the development of the Viscoelastic Characterization (VEC) test, from which the RM master curve can be developed. Material properties from the RM master curve can be easily determined and applied in the CMSE method. The modified repeated direct tension (RDT*) test removes rest periods and unwanted healing from the RDT test. The RDT* test also allows the dissipated pseudo strain energy (DPSE) to be separated into permanent deformation and fatigue cracking energies. The rate of change in DPSE associated with fatigue can then be applied in the CMSE method. Data sets for these tests are extensive and time consuming to analyze. Microsoft Excel spreadsheet macros were developed to reduce the time required for analysis from an estimated 10 hours to approximately 8 minutes. Testing of 14 different samples showed that the VEC and RDT* tests still required some adjustments in order to get accurate results. The rate of loading in the VEC test must be reduced to allow sufficient testing time to obtain the required data. The RDT* test requires a decrease in the controlling strain levels from 80 mu-epsilon and 350 mu-epsilon to 20 mu-epsilon and 175 mu-epsilon for the undamaged and damaged portions of the test, respectively. Testing of a sample using the new VEC and RDT* test recommendations showed that the recommended changes provided better results. Samples were undamaged where required and damaged portions of the test ran to completion without causing compression or sample failure. Material properties can be accurately determined and applied in the CMSE method.
SubjectAsphalt Fatigue Testing
Repeated Direct Tension
Calibrated Mechanistic with Surface Energy
Lawrence, James Jefferies (2009). Advanced Tools For Characterizing HMA Fatigue Resistance. Master's thesis, Texas A&M University. Available electronically from